Four doping conditions were explored for CdTe-based solar cells: p-type As and P, n-type Al, and no intentional doping. In each case, the CdTe absorber was alloyed with Se, but only near the normal front-side, light entry for the cells, while the dopants were added from the back. Cells with p-dopants showed efficiencies up to 20% with front-side illumination, but the n-doped and undoped ones were close to zero. With back-side illumination, this was reversed with undoped up to 8% and p-doped ones only about 2%. These results are explained by Kelvin-probe measurements of electric-field profiles, which showed that the diode field was near the front for the higher-efficiency p-doping, but near the back for undoped and n-doped.