Additive manufacturing enables lightweight sandwich structures with complex cellular cores, but the selection of material and process settings typically involves trade-offs among mechanical performance, cost, and sustainability. This study proposes an integrated multi-criteria decision-making framework to identify the most suitable configuration for Fused Filament Fabrication (FFF) sandwich structures featuring a gyroid triply periodic minimal surface (TPMS) core. Eight alternatives are evaluated by combining two materials (PLA and PLA–Flax biocomposite) with two extrusion temperatures (200 °C and 220 °C) and two infill densities (20% and 30%). Mechanical performance is represented by flexural strength obtained from three-point bending tests reported in a previously published experimental campaign, while economic and environmental indicators are quantified through material cost and printing energy consumption, respectively. Criteria weights are derived using the Analytic Hierarchy Process (AHP) based on expert judgment and consistency-ratio verification, and the alternatives are ranked using the TOPSIS method. The results highlight a clear dominance of PLA-based configurations under the adopted weighting scheme, with PLA printed at 200 °C and 20% infill emerging as the best compromise solution. PLA–Flax options are penalized by higher material cost, higher printing-process energy demand, and lower flexural strength in the investigated conditions. The proposed AHP–TOPSIS workflow supports transparent, data-driven selection of AM process–material combinations for gyroid sandwich structures, and it can be readily extended by including additional sustainability metrics (e.g., CO2-equivalent) and application-specific constraints. A sensitivity analysis under alternative weighting scenarios further confirms the robustness of the obtained ranking.
Parisi et al. (Sun,) studied this question.