To address surface defects and enhance the wear resistance of 316L stainless steel parts fabricated by Selective Laser Melting (SLM), this study applied shot peening (SP) surface treatment to the SLM-processed samples. Ball-on-disk tribological tests were systematically conducted under water-lubricated conditions to investigate the evolution of surface morphology, microstructure, microhardness, and tribological performance before and after SP. The results indicate that SP induced severe plastic deformation in the surface layer, effectively refining the coarse columnar crystals and melt pool structures characteristic of SLM, and forming a crystalline hardened layer with a depth of 70–80 μm. Consequently, the surface microhardness increased by 21.97% compared to the un-peened samples. Under loads of 20 N and 30 N, the coefficient of friction (COF) of the SP-treated samples decreased by 16.36% and 12.4%, while the wear rate was reduced by 17.09% and 14.9%, respectively. In this load range, the samples primarily exhibited uniform plowing and localized adhesive wear, demonstrating significantly improved resistance to plastic deformation and crack initiation. However, when the load increased to 40 N, intense stress and thermal effects diminished the strengthening benefits of SP, resulting in no significant difference in tribological performance between the SP-treated and untreated samples. At this stage, the dominant wear mechanism transitioned to severe plastic deformation, extensive delamination, and thermally induced adhesion.
Liu et al. (Wed,) studied this question.