Thermo-hydro-mechanical (THM) densification is an effective method for improving the mechanical performance of low-density, fast-growing hardwoods such as poplar. This study examined the bending performance of THM-densified poplar wood at different compression ratios (CR = 0%, 50%, 60%, and 65%), with emphasis on the effects of ultrasonic pretreatment (US) and thermal modification posttreatment (TM), applied individually and in combination. A paired sampling design was used to reduce material variability, and modulus of rupture (MOR) and modulus of elasticity (MOE) were evaluated using linear mixed-effects models (LMM). Bending tests were performed in accordance with EN 310:1993. Increasing the compression ratio led to substantial increases in MOR and MOE; compared with non-densified specimens, MOR increased by approximately 240% and MOE by about 140% at CR = 65%, confirming densification as the dominant factor controlling bending performance. US did not affect non-densified wood but significantly enhanced MOR and MOE after densification, particularly at CR = 50%. In contrast, TM consistently reduced MOR and, to a lesser extent, MOE across all compression ratios. The results demonstrate that the bending performance of densified poplar wood is governed by both compression ratio and compression-dependent treatment effects.
Veizović et al. (Sun,) studied this question.