This paper reviews the enhancement mechanisms of fatigue performance in titanium alloys processed by laser shock peening (LSP). Because of the redistribution of residual stress and micro-crack and pore behavior, micro–nanostructure evolution and surface roughness effect are systematically discussed. LSP induces beneficial compressive residual stresses at the surface, effectively suppressing crack initiation and propagation. Notably, the nanostructures induced by this process—including nanotwins, dislocations, stacking faults, and nanocrystals—collectively enhance the material’s mechanical hardness, strength, and fatigue resistance. Furthermore, LSP reduces porosity, alters pore morphology and alters crack initiation sites, thereby increasing the crack propagation threshold. However, the influence of LSP on material toughness remains a subject of debate. The insights provided herein offer valuable theoretical guidance for the development of high-performance titanium alloys and further optimization of LSP technology.