This study demonstrates that compressive strength in cement-stabilized rammed earth is governed by conditional, threshold-controlled interactions rather than by intrinsic mineralogical effects. A B + K (beidellite + kaolinite) content exceeding 15% defines a low-strength regime (median ≈ 44.6 kN), whereas B + K ≤ 5% allows medians above 90 kN under 7% forming moisture. Quartz-rich fractions show a global correlation of r = 0.71. The Kruskal–Wallis test confirms strong clay grouping influence (H = 72.78, p 15%) exerts a negative influence under elevated forming moisture (8%), whereas the effect of 1:1 and 2:1 clay minerals differs depending on their hydro-affinity and moisture regime. However, subgroup analyses reveal frequent reversals in both magnitude and sign of correlations, proving that mineral effects depend critically on cement dosage and moisture regime, revealing discrete strength regimes defined by hierarchical interactions between moisture, cement content, and mineralogical thresholds. The combined beidellite–kaolinite content was classified into ≤5%, 5–15%, and >15% groups. Specimens with B + K > 15% consistently formed a low-strength regime, with a median destructive load of approximately 44.6 kN (≈1.1–1.3 MPa depending on cross-sectional area). In contrast, mixtures with B + K ≤ 5% achieved median loads above 90 kN (≈2.5–3.0 MPa). Quartz-rich fractions showed a strong global positive correlation with strength (r = 0.71), while the grouped clay fraction exhibited a highly significant effect (Kruskal–Wallis H = 72.78, p < 0.001). A regime shift was observed between 7% and 8% forming moisture, where quartz correlation changed from strongly positive (r ≈ 0.70) to negative (r ≈ −0.69). Increasing cement content from 6% to 9% significantly improved strength (H = 12.30, p = 0.0005), although this effect diminished when B + K exceeded 15% or forming moisture reached 8%. Association rules further confirm that high or low strength emerges only from specific multivariate combinations. The results show that mineralogy influences CSRE strength primarily through interaction with technological parameters, providing a robust basis for regime-based interpretation and rational mixture design.
Narloch et al. (Wed,) studied this question.