This study investigates the fatigue failure of fiber-reinforced rubber used in automotive shock-absorbing elements subjected to cyclic loads. A quantitative simulation model integrated with material analysis to predict the service life and performance decay of these viscoelastic dampers was introduced. Failure is governed by a degradation factor that models accumulating fatigue damage and results in a predictable, cyclic loss of maximum force capacity; specifically, the model accurately predicts a 36.3% reduction in peak force (from 111.44 N to 70.97 N) over the first 10 fatigue cycles. Crucially, the model incorporates the non-linear stiffness behavior caused by a fiber pull-out mechanism, which transitions load resistance from high elastic integrity to lower frictional forces post-critical displacement. These findings establish a direct, quantitative link between microstructural failure (verified via SEM) and observed performance decay, offering key insights for maintenance planning and material selection.