This study systematically investigated the bearing capacity and failure mechanisms of ultra-high-performance concrete (UHPC) pipe jacking structures using three-edge bearing tests and numerical simulations. Full-scale double-layer reinforced pipes had an inner diameter of 2.5 m and wall thicknesses of 180 mm (P1) and 200 mm (P2). The tests showed that the failure process can be divided into four stages: elastic deformation, crack propagation, reinforcement yielding, and ultimate failure. Increasing the wall thickness significantly improved performance: P2 had a cracking load 52.73% higher and an ultimate bearing capacity 5.7% higher than P1, with better deformation resistance and crack control. A theoretical model considering the plastic hinge mechanism at the pipe crown was developed, treating the three-edge load as an equivalent distributed plate load. The calculated results agreed well with experimental measurements. An ABAQUS finite element model successfully reproduced the full mechanical response from initial loading to failure. Parametric analysis indicated optimal performance at a hoop reinforcement ratio of approximately 1.4%. Even at 0.6%, the ultimate bearing capacity reached 367 kN/m, meeting current design code requirements. This study is novel in conducting full-scale UHPC pipe jacking tests, proposing a theoretical model accounting for crown plastic hinges, and establishing a finite element method that reproduces the entire failure process. Optimizing wall thickness and hoop reinforcement can enhance structural safety and durability, providing guidance for the design and engineering of pipe jacking structures.
Ma et al. (Tue,) studied this question.