Preparation and Self-Healing Properties of Polyurethane with Dual Dynamic Covalent Bonds

Dynamic covalent bonds are commonly used to maintain the self-healing properties of polyurethanes and facilitate resource recycling. However, relying on a single type of dynamic covalent bond often makes it difficult to effectively regulate both mechanical and self-healing properties across a wide temperature range. In this study, a self-synthesized chain extender containing disulfide bonds was introduced into a polyurethane system, leading to the development of a novel dual-dynamic covalent bond self-healing polyurethane (SSDA-PU). Innovatively, this SSDA-PU demonstrates self-healing properties across a wide temperature range. The successful synthesis of the chain extender and the incorporation of both disulfide bonds and Diels–Alder (DA) bonds were confirmed using FTIR and Raman spectroscopy. The physical characteristics and self-healing performance were comprehensively evaluated through multi-scale testing and characterization, including thermogravimetric analysis (TGA), dynamic mechanical analysis (DMA), hardness testing, mechanical tensile tests, and self-healing experiments. The underlying synergistic self-healing mechanism was subsequently elucidated. Findings showed that a higher R-value (isocyanate index) in SSDA-PU leads to over-crosslinking, while an R-value of 1.7 achieves the best overall mechanical performance, with tensile strength and elongation at break reaching 21.1 MPa and 755.17%, respectively. Additionally, SSDA-PU demonstrated the capacity for multiple healing cycles, with an initial self-healing efficiency of 90.38%, which remained notably high at 59.21% even after three damage-healing cycles. Importantly, SSDA-PU exhibited healing capabilities even at relatively low temperatures. Cracks in SSDA-PU can be effectively repaired through the synergistic action of disulfide bond exchange, hydrogen bond dissociation, and thermally reversible DA reactions. SSDA-PU also shows excellent recyclability, offering valuable insights for the practical engineering application of functional polyurethanes.