Titanium alloys, particularly β-type Ti-13Nb-13Zr, are promising biomedical materials due to their low elastic modulus and excellent biocompatibility. However, their bioactivity needs improvement for better bone integration. In this study, a calcium-phosphate (Ca/P) coating was prepared on a Ti-13Nb-13Zr alloy via micro-arc oxidation (MAO) in an electrolyte containing calcium acetate and dipotassium hydrogen phosphate. The effect of applied voltage (300 V, 400 V, and 500 V) on the phase composition, surface morphology, and in vitro bioactivity of the coatings was investigated. Surface characterization was performed using scanning electron microscopy (SEM), X-ray diffraction (XRD), and energy-dispersive spectroscopy (EDS). The results show that increasing the voltage increased the surface roughness, average pore size, and rutile TiO2 content in the coating. The Ca/P ratio in the coating approached 1.67 at 500 V, similar to that of natural bone. After immersion in simulated body fluid (SBF) for 20 days, the coating formed at 500 V induced the highest deposition of hydroxyapatite (HA), completely covering the microporous surface. These findings indicate that MAO treatment at 500 V significantly enhances the bioactivity of the Ti-13Nb-13Zr alloy, making it a promising candidate for orthopedic implants.
Liu et al. (Thu,) studied this question.