To overcome active site blockage and poor interfacial contact in traditional syntheses, PtNi bimetallic nanoparticles were grown in situ on a microporous carbon paper via pulse electrodeposition. Firstly, the impact of deposition potential was investigated. The results indicate that the deposition potential significantly modulates the surface Pt0/Pt2+ ratio; concurrently, a shift toward more negative potentials intensified nanoparticle agglomeration. The effects of the duty cycle were investigated at an optimal deposition potential of −0.95 to −0.4 V. A duty cycle of 30% yielded the optimal Pt0/Pt2+ ratio. Furthermore, TEM revealed a coexisting strain profile of bulk PtNi lattice contraction and localized expansion at peripheral Pt (111) facets. This synergistic tuning of surface valence and strain optimizes the thermodynamic balance between oxygen adsorption and intermediate desorption on Pt sites. In summary, the optimal catalyst, prepared at a deposition potential of −0.95 V and a duty cycle of 30%, showed the best reaction behavior in the oxygen reduction reaction with an initial onset potential of 0.92 V (vs. RHE). After 5000 cycles of testing, the catalyst showed a constant durability, with the onset potential degrading only marginally to 0.87 V. This work successfully demonstrates that the surface morphology and valence states of the catalyst can be effectively tailored by regulating the pulse voltage and duty cycle.
Bu et al. (Fri,) studied this question.