Aramid fiber reinforced polymers (AFRPs) are widely used in aerospace and defense structures because of their high specific strength, impact resistance, and damage tolerance. However, severe burr formation during machining remains a major obstacle to achieving high surface integrity and dimensional accuracy. In particular, the mechanism by which tool edge radius affects burr formation in AFRP cutting has not yet been clarified quantitatively. To address this issue, this study develops an analytical model for the orthogonal cutting of AFRPs to reveal the burr formation mechanism associated with tool edge radius. The model, established on the basis of contact mechanics and fracture theory, predicts fiber deflection, cutting force evolution, fracture behavior, and burr length under different contact and boundary conditions. The results show that tool edge radius governs burr formation through a contact–state transition mechanism. When the edge radius is below a critical threshold, localized point-contact-like interaction promotes stress concentration and fiber fracture, leading to relatively clean material removal. When the edge radius exceeds this threshold, the interaction evolves toward extended contact and sliding, which suppresses complete fiber fracture and results in pronounced burr retention. Experimentally, increasing the edge radius from 5.6 μm to 110.3 μm increased the maximum burr height from 3.19 μm to 83.58 μm, corresponding to an increase of approximately 2520%. The predicted burr evolution agrees well with the experimental observations in both trend and characteristic magnitude. This study provides a mechanistic and predictive understanding of burr formation in AFRP machining and offers practical guidance for cutting edge preparation, tool wear control, and process optimization in high-quality composite machining.
Cao et al. (Fri,) studied this question.