To facilitate the development of low-cost LTCC substrate materials and the high-value utilization of industrial tailings, α-cordierite glass-ceramics with varying Na2O additions were prepared from perlite tailings as the main raw material via the melt-quenching method followed by sintering-induced crystallization. The synergistic effects of sintering temperature and Na2O addition on the parent glass structure, crystallization behavior, and properties were systematically investigated. The results demonstrated that the addition of Na2O effectively depolymerized the degree of network polymerization of the parent glass, altered the crystallization pathway of cordierite crystal, and promoted the densification of glass-ceramics at lower sintering temperature. The calculations of crystallization kinetics revealed that the crystallization process of α-cordierite was mainly dominated by three-dimensional bulk growth, and its nucleation mechanism changed from “site saturation” to “continuous nucleation” with the increase of Na2O addition. The α-cordierite glass-ceramics sintered at 850 °C with 0.6 wt.% Na2O addition exhibited the optimal comprehensive properties, including low dielectric constant (5.82 @ 10 MHz) and dielectric loss (1.80 × 10−2 @ 10 MHz), high flexural strength (147.3 MPa), a Vickers hardness (9.01 GPa), and suitable coefficient of thermal expansion (2.96 × 10−6 K−1, close to Si). The glass-ceramics are expected to be an ideal candidate for low-cost LTCC substrate materials.
Wang et al. (Sat,) studied this question.