Objective: This work aims to reduce the surface tension of an aluminum–silicon alloy melt by adding different amounts of the Zn element, thus improving the coatability and coating quality of hot-dip aluminum plating on steel plates. Method: Wetting experiments were conducted at 1023 K using a modified sessile drop method. Conclusions: The addition of the Zn element can reduce the surface tension of the Al-Si alloy, thus decreasing the wettability of the Al-Si alloy. Zn vapor can break down the surface oxide film to expose the fresh melt. The wettability of the Al-10Si alloy on interstitial-free (IF) steel and surface tension were investigated using the modified sessile drop method at 1023 K. Axisymmetric Drop Shape Analysis software was utilized to calculate the contact angles of the Al-10Si-xZn/Al2O3 and Al-10Si-xZn/IF steel systems (x ranges from 0 wt.% to 5 wt.%). Moreover, the microtopography and microstructure of surfaces and cross-sections were analyzed by means of an energy-dispersive spectrometer and scanning electron microscope. The results indicated that the surface tension of the alloy melt gradually decreases with an increase in Zn content, ranging from 874 to 760 mN/m. The contact angle of the Al-10Si-xZn alloy melt on IF steel also progressively decreases with increasing Zn content, which is attributed to the lower surface tension of Zn. This study also discovered that the Zn element can disrupt the oxide film of the Al-10Si alloy, exposing the fresh melt and thereby reducing the surface tension of the alloy liquid, thus enhancing wettability. The addition of Zn might be capable of improving the hot-dip aluminizing coatability of steel plates and the quality of the coating.
Chen et al. (Fri,) studied this question.