To address the issues of high cutting temperatures and severe tool wear during titanium alloy machining, this study proposes a hybrid surface modification strategy combining micro-textures and multicomponent titanium nitride (TiN)-based coatings on cemented carbide tools. Using YG8 cemented carbide as the substrate, micro-dimple textures were fabricated by fiber laser, and three coatings with different architectures (TiAlSiN, TiSiN/TiAlN, and TiSiN/TiAlSiN/TiAlN) were deposited via multi-arc ion plating technology. Based on a two-factor (texture diameter and texture spacing) and three-level orthogonal experiment, the evolution behaviors of surface morphology, phase composition, and mechanical properties of the textured multicomponent TiN-based coatings were systematically characterized and comparatively analyzed. The results reveal that: compared to the monolithic-structured TiAlSiN coating, the TiSiN/TiAlSiN/TiAlN and TiSiN/TiAlN composite coatings with multilayered composite structures can effectively relieve the residual stress inside the film–substrate system, and significantly suppress the phenomena of coating cracking and localized spallation caused by irregular protrusions of the recast layer at the micro-texture edges. X-ray diffraction (XRD) and crystallite size analyses indicate that the amorphous Si3N4 phase promoted by the Si element in the composite coatings effectively impedes the growth of TiN columnar crystals, achieving significant grain refinement. Mechanical property tests confirm that the existence of multicomponent composite interfaces effectively hinders dislocation movement. Among them, the textured TiSiN/TiAlSiN/TiAlN composite coating exhibits the optimal comprehensive performance; its microhardness, nanohardness, and H/E ratio (characterizing the resistance to plastic deformation) are increased by 17.94%, 8%, and approximately 45%, respectively, compared to those of the textured TiAlSiN coating. This study deeply elucidates the synergistic strengthening and toughening mechanisms between micro-texture parameters and the internal structures of the coatings, providing important theoretical guidance and experimental data support for the surface design of long-lifespan tools oriented towards the high-efficiency machining of titanium alloys.
Tong et al. (Tue,) studied this question.