Modification of PLA with functional nanoparticles is a promising approach for imparting new properties to the material. In this work, titanium nanoparticles (Ti NPs) and titanium dioxide nanoparticles (TiO2 NPs) were synthesized by laser ablation and characterized by dynamic light scattering, spectrophotometry, and transmission electron microscopy. The average hydrodynamic diameter of Ti NPs was 12 nm, while that of TiO2 NPs was 24 nm; both dispersions possessed a positive zeta potential (23–27 mV) and spherical morphology. L-PLA composite films containing 0.1 wt.% Ti NPs or TiO2 NPs were obtained by solution casting. Atomic force and modulation-interference microscopy confirmed the uniform distribution of nanoparticles within the polymer matrix, although partial aggregation was observed. The introduction of TiO2 NPs increased the water contact angle. Mechanical testing revealed a significant reinforcing effect: the addition of 0.1 wt.% NPs increased the Young’s modulus by 62–68% and the ultimate tensile strength by 16–18% while maintaining a ductile fracture pattern with elongation at break up to ~8%. Both types of composites generated reactive oxygen species (ROS) in aqueous solutions: Ti NPs increased H2O2 production by 5.5 times and TiO2 NPs by 4.9 times, and they also induced the formation of hydroxyl radicals. The accumulation of 8-oxoguanine in DNA and long-lived oxidized protein species confirmed the materials’ ability to cause oxidative damage to biomacromolecules. For E. coli, growth inhibition reached 40.5% (for composites with Ti NPs) and 71% (for composites with TiO2 NPs). The effect was even more pronounced for S. aureus, where inhibition levels were approximately 70% and 80%, respectively; flow cytometry confirmed the strong bactericidal effect, showing that materials containing TiO2 NPs increased the proportion of dead cells to 25% for E. coli and ~68% for S. aureus. Cytotoxicity assessment on human fibroblasts (HSF) demonstrated the high biocompatibility of neat L-PLA and composites with Ti NPs (viability > 95%) and with TiO2 NPs (viability ~93%). The obtained results indicate that L-PLA-based composites with Ti NPs and TiO2 NPs exhibit pronounced ROS-mediated antibacterial activity without additional UV irradiation. These findings position these materials as highly promising candidates for active biodegradable food packaging to extend shelf-life and for biomedical devices, such as wound dressings and implants, where reducing the risk of bacterial colonization is critical.
Burmistrov et al. (Sun,) studied this question.