A ternary CdS–MoS2–rGO photocathode was developed to enhance visible light-driven hydrogen evolution through interfacial heterostructure engineering. The composite was fabricated via a solution-based deposition method followed by thermal conversion, resulting in crystalline CdS and MoS2 phases that were uniformly integrated within a conductive reduced graphene oxide (rGO) framework. Structural and surface analyses (XRD and XPS) confirmed the coexistence of Cd2+, Mo4+, and S2− chemical states without detectable secondary phases. Photoelectrochemical measurements revealed that the ternary architecture significantly improves charge separation efficiency and interfacial charge-transfer kinetics compared to binary and single-component films. The CdS–MoS2–rGO photocathode exhibited the highest photocurrent density, reduced charge-transfer resistance, and favorable Tafel slope under visible-light irradiation (0.25 sun, neutral electrolyte). Gas chromatography measurements verified that these electrochemical enhancements translate into increased hydrogen production rates, following the trend: CdS–MoS2–rGO > CdS–rGO > MoS2–rGO >> rGO. Applied bias photon-to-current efficiency (ABPE) analysis further confirmed improved photon utilization efficiency in the ternary system. The enhanced performance is attributed to synergistic integration of CdS (light harvesting), rGO (rapid electron transport), and MoS2 (catalytic edge sites), which suppresses recombination and accelerates proton reduction kinetics. These findings demonstrate that rational multi-component heterostructure design is an effective strategy for improving hydrogen evolution rate under mild operating conditions.
Alsultan et al. (Wed,) studied this question.