Wollastonite is a natural meta-silicate mineral material with fibrous characteristics. In this paper, wollastonite with different aspect ratios obtained after grinding was used as a mineral admixture to replace cement for preparing ultra-high-toughness cement-based composites (UHTCCs). The effects of wollastonite on the fluidity, compressive strength, flexural strength, and tensile properties of UHTCCs were investigated, and the crack morphology and micro-topography of the tensile specimens after fracture were observed. The experimental results show that when the wollastonite replacement ratio exceeds 4%, it exerts a negative effect on the fluidity of UHTCCs, and wollastonite with a larger aspect ratio has a more significant negative impact. Relying on the bridging effect, replacing cement with wollastonite can significantly improve the flexural strength and compressive strength of UHTCCs. However, when the replacement ratio exceeds 6%, the strength enhancement effect of wollastonite with a larger aspect ratio begins to decrease. When the cement replacement ratio of wollastonite is up to 6%, it can increase the initial cracking strength, tensile strength and tensile strain of UHTCCs. At the same replacement ratio, wollastonite with a larger aspect ratio shows a better reinforcing effect. According to the observation of post-fracture crack morphology, the cracks of UHTCCs change from the original smooth cracks to tortuous ones after cement is partially replaced by wollastonite. Replacing a part of cement with wollastonite optimizes the performance relationship among PE fibers, the matrix, and the PE fiber–matrix interface, and it enhances their synergistic effect. This not only raises the initial tensile cracking strength of UHTCCs but also improves its tensile strain. In particular, wollastonite with a larger aspect ratio exhibits a more pronounced reinforcing effect.
Wang et al. (Thu,) studied this question.