This study investigates the influence of the depth of lattice-array micro-pillar surface microstructures on the cavitation erosion (CE) of nickel-aluminum bronze (NAB) in a saline solution using both experimental and simulation methods. Mass-loss measurements, electrochemical tests, and morphological characterizations (SEM, white-light interferometry, EBSD) were conducted to clarify the erosion, corrosion, and synergistic components. Pressure distribution, vapor volume fraction, and bubble dynamics were revealed by numerical simulation in the cavitation region. Results show that shallow microstructures (0.02 and 0.07 mm depths) significantly reduce the CE by up to 74% compared to the smooth surface. This structure can form a shielding field and suppress the mechanical erosion component. In contrast, deep microstructures (0.18 and 0.22 mm depths) aggravate CE, which is attributed to increased bubble nucleation and localized vapor content, and intensified pressure difference. The pure erosion component dominates the damage, followed by synergistic action, and the pure corrosion component is the least. This trend is independent of the change in the microstructure. These findings extend the knowledge on how to design the microstructure depth to alleviate CE.
Yang et al. (Mon,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: