Materials derived from renewable and recycled resources offer a promising route toward more sustainable thermoset composites. In this study, waste poly(ethylene terephthalate) (PET) was depolymerized by glycolysis with propylene glycol to obtain a glycolysate, and subsequently polycondensed with biobased propylene glycol, maleic anhydride, and trimethylolpropane diallyl ether to synthesize biobased UV-curable unsaturated polyester resin (UV-bUPR). The composites were prepared with acryloyl-modified Kraft lignin (KrL-A) as a reactive bio-filler using a dual-curing approach, in which rapid UV curing was followed by thermal/redox post-curing to improve conversion and network homogeneity. The structure of the synthesized resin and composites was confirmed by FTIR and NMR spectroscopy. Mechanical properties were evaluated by tensile testing and hardness measurements, while morphology and fracture behavior were analyzed by scanning electron microscopy. The unmodified lignin decreased tensile performance due to limited compatibility with the polyester matrix and the formation of interfacial defects and agglomerates. In contrast, KrL-A exhibited improved dispersion and stronger filler–matrix interactions, resulting in superior mechanical performance. The most pronounced effect of lignin modification was observed at 15 wt.% filler loading, where the tensile strength reached 27.83 MPa, compared with 13.91 MPa for the corresponding unmodified system. The developed composites also showed improved sustainability, assessed through the E-factor, due to the combined use of recycled PET and renewable lignin.
Dagale et al. (Tue,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: