The CNT-supported nanodispersed Pt–Mo catalysts for the ethanol electrooxidation reaction in the alkaline solution are synthesized and their characteristics are studied. Based on the XPS studies in a wide range of platinum content (10–40 wt %), it is found that in the composition of the catalysts, platinum is predominantly in the metallic state, and molybdenum is in the hexavalent form, probably in the form of MoO3 oxide. According to the XRD and electrochemical studies, the Pt/CNT and PtMo/CNT catalysts with equal platinum contents (~20 wt %) are characterized by similar platinum crystallite sizes (5–10 nm) and electrochemically accessible surface areas (23–26 m2/gPt). This indicates that platinum is not shielded by the molybdenum compounds. When the platinum content increases above 20 wt %, the Pt:Mo atomic ratio increases (the nominal ratio is 1:1), which may be due to the decoration of molybdenum oxide with platinum nanoparticles. A study of the kinetics of the ethanol electrooxidation reaction showed that the activity of the PtMo/CNT system is higher than that of the Pt/CNT catalyst. However, the efficiency of platinum use decreases as its content in the PtMo/CNT system increases from 10 to 40 wt %. On the other hand, the systems containing 20–40 wt % Pt exhibit the highest activity per unit catalyst weight, making them very promising for use as a component of the anode active layer of a fuel cell. The tests of the alkaline ethanol fuel cell based on the synthesized catalysts show the maximum power density of 29 mW/cm2, which corresponds to the level of the best literature parameters under similar experimental conditions.
Корчагин et al. (Thu,) studied this question.