Mechanically activated pyrite plays an important role in gold extraction and coal utilization, but its reactivity may change markedly during storage. This study investigates how air deactivation during storage affects the crystal structure and subsequent thermal decomposition behavior of mechanically activated pyrite. Pyrite was mechanically activated and then stored in air for 0, 7 and 180 days. X-ray diffraction (XRD) combined with Rietveld refinement was used to characterize variations in lattice parameters and unit-cell-related structural features, while non-isothermal thermogravimetric–differential scanning calorimetry (TG-DSC) under an argon atmosphere, together with the Flynn–Wall–Ozawa (FWO) method, was applied to evaluate the decomposition kinetics. Air deactivation induced a non-monotonic evolution of lattice parameters and unit-cell volume, which is attributed to combined effects of residual stress relaxation and air-induced surface-related modification during storage. All samples exhibited two mass-loss stages during heating, reflecting stepwise thermal decomposition, and their decomposition behavior varied systematically with deactivation time. The apparent activation energy depended on both conversion fraction and deactivation degree, and nucleation-and-growth-type mechanisms were found to dominate the decomposition process, with their relative contributions evolving with storage time. These results clarify how prior air-deactivation history influences the structural evolution and subsequent thermal decomposition behavior of mechanically activated pyrite and provide useful insight for its storage and utilization in related processes.
Chen et al. (Fri,) studied this question.