ABSTRACT Alkali vapor corrosion is critical for refractories used in the kilns and furnaces of diverse high‐temperature processing and manufacturing sectors such as gasifiers, cement production, and glass making. Gahnite (ZnAl 2 O 4 ) is being investigated as a potential chrome‐free refractory because of its similarity with the structure and properties of magnesium aluminate (MgAl 2 O 4 ) spinel. The alkali vapor corrosion of ZnAl 2 O 4 , MgAl 2 O 4 , and Mg 0.5 Zn 0.5 Al 2 O 4 was studied, according to ASTM C987‐10, at 1371°C for 24 h using sodium carbonate (Na 2 CO 3 ). The surface and the polished cross‐sections of the corroded ZnAl 2 O 4 , MgAl 2 O 4 , and Mg 0.5 Zn 0.5 Al 2 O 4 specimens were analyzed using x‐ray diffraction (XRD), microscopy, and energy‐dispersive spectroscopy (EDS) techniques. MgO in MgAl 2 O 4 , ZnO in ZnAl 2 O 4 , Mg 0.77 Zn 0.23 O, and NaAlO 2 were detected as the corrosion products for these specimens. The extent of corrosion substantially varied among the specimens despite the similarity in the corrosion products. The corrosion resistance increased in the following order: Mg 0.5 Zn 0.5 Al 2 O 4 > MgAl 2 O 4 > ZnAl 2 O 4 . The formation of a dense MgO and Mg 0.77 Zn 0.23 O layer for MgAl 2 O 4 and Mg 0.5 Zn 0.5 Al 2 O 4 , respectively, contributed to their superior resistance to alkali vapor corrosion. The underlying corrosion mechanisms are discussed based on experimental observations supported by thermodynamic analysis. Additionally, the results suggest that a partial Zn 2+ substitution for Mg 2+ in MgAl 2 O 4 can enhance the resistance to alkali vapor corrosion.
Ramteke et al. (2026) studied this question.