In this work, we report the fabrication and characterization of single-film and double-film composite epitaxial garnet structures based on single-crystalline films (SCFs) and bulk single-crystal (SC) scintillators for enhanced α–γ discrimination in mixed radiation fields. These composite scintillators consist of TbAG:Ce and YAG:Ce SCFs grown by liquid-phase epitaxy (LPE) on Czochralski-grown Gd3Ga2.5Al2.5O12 (GAGG:Ce) bulk SC substrates. Single- and double-film architectures were designed to optimize the energy absorption and pulse-shape discrimination (PSD) performance for low-penetrating α-particles and high-energy γ-rays. Energy calibration was performed using different γ-ray sources (57Co, 51Cr, and 137Cs), enabling the conversion of detector signals to a calibrated electron-equivalent energy scale (keVee). Integration gates were systematically optimized, yielding maximum figures of merit (FOM) of 1.4 for the GAGG:Ce SC substrate, 1.9 for the single-film composite, and 5.0 for the double-film composite, demonstrating a progressive improvement in α–γ discrimination with increasing structural complexity. Two-dimensional PSD density maps reveal well-separated α and γ events, with the highest separation observed for the double-film composite. These results indicate that the engineering of LPE-grown composites provides tunable scintillation decay profiles, enhanced temporal separation, and increased light yields, making them promising candidates for applications such as mixed radiation field detection, dosimetry, and radiation monitoring.
Bachiri et al. (Tue,) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: