ABSTRACT Uranium borides are promising candidate fuel forms for use in advanced nuclear reactors due to their high thermal conductivity and potential for dual use as both fuel and burnable absorber. In this work, uranium tetraboride () and uranium monoboroncarbide (UBC) composite were synthesized by using industrially scalable carboborothermic reduction method. The final uranium boride phase composition is sensitive to the sample holding crucibles ( and graphite) such that graphite supply excess carbon, promoting the formation of a predominant UBC phase. The high‐temperature in situ synchrotron X‐ray diffraction of pristine –UBC show persistence , UBC, and phases while preoxidized –UBC leads to predominant and formation due to progressive oxidation and boron loss at high temperature. The oxidation behavior was further characterized using thermogravimetric analysis, allowing direct comparison with other potential accident tolerant fuels such as , , UC, and UN. The –UBC shows higher uranium loading than monolithic and demonstrates promising oxidation behavior at high temperature, pointing to its potential as an improved uranium boride‐based fuel form.
Moeykens et al. (Fri,) studied this question.