The construction sector’s drive for sustainability has increased the use of Cross-Laminated Timber (CLT), yet its structural reliability is governed by the integrity of the adhesive bond line. This study evaluates the influence of three one-component polyurethane (PUR) formulations (R1, R2, R3) on the adhesion performance of maritime pine CLT. To isolate adhesive-related effects, lamellas were mechanically classified by modulus of elasticity (MOE) and randomly allocated within stiffness classes. Adhesive characterization through ABES, FTIR, and DSC revealed that R3 exhibited slower cure kinetics (t0 = 5482 s) but higher thermal stability. Mechanical testing showed that all formulations developed structurally effective dry bonds with shear strengths exceeding 7.1 MPa, with R3 achieving significantly higher dry shear and interlaminar strength. However, 24 h water immersion caused a catastrophic strength reduction exceeding 95% across all formulations, shifting the failure mode from the wood substrate to the adhesive layer. DSC analysis identified glass transition temperatures between 28 °C and 32 °C, which are consistent with the potential for moisture-induced plasticization near service temperatures. These results indicate that while slower-curing formulations like R3 enhance bond quality in dense softwoods due to improved interphase formation, all evaluated PUR systems showed significant vulnerability to saturated conditions, suggesting that adequate moisture protection is essential for maritime pine CLT applications.
Cavalcante et al. (Wed,) studied this question.