ABSTRACT Hafnia‐based ferroelectrics hold promise to reduce energy demand for computing by enabling compute‐in‐memory and as non‐volatile memories. The ferroelectric phase in this material system is, in part, stabilized by oxygen vacancies. While oxygen vacancies may be a necessity for phase stability, they limit device endurance through diffusion and accumulation into conducting channels. Herein, it is shown that oxygen diffusion is spatially variable within individual grains of ferroelectric hafnium zirconium oxide (HZO). Using 18 O tracers and finite difference modeling, it is shown that grain boundaries and regions near electrode interfaces allow for relatively rapid oxygen diffusion, with values as much as 10 4 larger than the grain cores. Further, the selection of electrode material affects the diffusion coefficients across all microstructural regions. HZO films in contact with TiN electrodes result in more oxygen‐deficient HZO films and higher oxygen diffusion coefficients. Tungsten electrodes result in fewer vacancies and lower diffusion coefficients. Diffusion activation energy differences between the HZO with the two electrodes is reconciled by differing populations of charged and uncharged oxygen vacancies. This insight into the local vacancy populations and diffusion pathways provides a platform for designing hafnia‐based films, deposition processes, and integration strategies to reduce vacancy gradients and improve performance.
Shvilberg et al. (Wed,) studied this question.