In this study, the two-dimensional aligned steel fiber-reinforced micro-expansive concrete (2D) was prepared, aiming to address the inherent vulnerabilities of concrete, such as early-age shrinkage cracking and low tensile ductility. For this purpose, the steel fibers and expansive agent were utilized. Furthermore, the planar rotating magnetic field was used to randomly distribute the steel fibers in a two-dimensional plane. In order to verify its superior mechanical and shrinkage properties, the compressive, fracture and drying shrinkage tests were carried out. The results demonstrate that the 2D alignment method enhances the fiber utilization efficiency. Compared with fiber-free groups, the compressive strength and fracture parameters of specimens incorporating steel fibers were improved. Furthermore, compared with randomly distributed steel fiber-reinforced micro-expansive concrete (RD), the 2D alignment method made the cubic compressive strength and fracture energy improve 8–14.2% and 19.4–110%, respectively. Additionally, the advantage of the fiber 2D alignment method was also reflected in the inhibition of drying shrinkage. Compared with normal concrete, the 180-day shrinkage strain of the 2D1.2 group was reduced to 200 με (only 19.5% of that of normal concrete, or 30.6% of that of micro-expansive concrete). Mechanistically, these superior performances are fundamentally governed by a coupling effect: chemical shrinkage compensation and physical alignment constraint.
Qing et al. (Sun,) studied this question.