This study investigates the synthesis and physicochemical characterization of biolubricant base oils derived from sunflower oil methyl esters (SUNOMEs) via transesterification with trimethylolpropane (TMP) using guanidine carbonate (GNDC) as a green and efficient catalyst. The transesterification process was optimized to achieve high conversion and desirable physicochemical properties suitable for lubrication applications. The synthesized esters were characterized by viscosity, density, pour point, and oxidation stability, confirming their suitability as environmentally friendly lubricants. Reaction parameters, such as catalyst concentration (3.0–5.0 wt%), were optimized under both solvent-free and vacuum-assisted conditions. The use of guanidine carbonate achieved enhanced physicochemical properties with significantly reduced reaction times (≈6 h) and eliminated soap formation. The resulting TMP triesters exhibited kinematic viscosities in ranges of 41.27–52.73 cSt (40 °C) and 8.668–10.02 cSt (100 °C), a viscosity index in the range of 180–196, and excellent oxidation stability (RSSOT: up to 54.27 min). Fourier transform infrared (FTIR) analysis confirmed the formation of complete triester structures with characteristic carbonyl and C–O stretching bands at 1735 cm−1 and 1050 cm−1, respectively. Spectra showed also distinct stretching vibrations near 1640–1670 cm−1 and 3300–3400 cm−1, which correspond to amide carbonyl and N–H characteristic groups. The tribological performance was evaluated using Four-Ball Standard Test Method, demonstrating significant improvements compared to commercial mineral oils. The results indicate that guanidine carbonate is an effective catalyst for producing sunflower-oil-derived esters with favorable lubricating properties, highlighting their potential as sustainable biolubricants for industrial applications.
Filon et al. (Tue,) studied this question.