Hydrogenation Behavior of a Fine-Grained Ti-V-Zr-Nb-Mo-Hf-Ta-W Refractory High-Entropy Alloy Produced by Plasma-Assisted Centrifugal Atomization

In this work, the hydrogenation behavior of a near-equiatomic Ti-V-Zr-Nb-Mo-Hf-Ta-W refractory high-entropy alloy (R-HEA) exposed to pressurized hydrogen has been thoroughly investigated. Isothermal gas-phase hydrogen absorption experiments have been performed and a maximum uptake of 1.13 wt.% H has been achieved after exposure to a pure H2 atmosphere at 350 °C and 60 bar H2 for 6 h. This hydrogen absorption capacity is rather low compared to previous literature, where capacities as high as 2.7 wt.% have been reported. The presence of two distinct (Hf,Zr)-mixed oxides at the surface of the particles has been deduced from X-ray diffraction analyses and identified as the main reason for the relatively low H uptake and the minimal impact onto the mechanical integrity of the R-HEA after hydrogenation. The results hereby reported suggest that R-HEAs containing strong oxide-forming elements such as Hf, Zr, and Ti undergo surface hydrogenation-regeneration upon intermittent exposure to a hydrogen atmosphere. The cyclic nature of such phenomena should be further investigated, as it could lead to the development of novel, self-regenerating protective materials against hydrogen diffusion and embrittlement to be potentially used as permeation barriers.