The piezoelectric properties of relaxor based ferroelectric single crystals, such as Pb(Zn1/3Nb2/3)O3–PbTiO3 and Pb(Mg1/3Nb2/3)O3–PbTiO3 were investigated for electromechanical actuators. In contrast to polycrystalline materials such as Pb(Zr,Ti)O3, morphotropic phase boundary compositions were not essential for high piezoelectric strain. Piezoelectric coefficients (d33’s)2500 pC/N and subsequent strain levels up to 0.6% with minimal hysteresis were observed. Crystallographically, high strains are achieved for 〈001〉 oriented rhombohedral crystals, although 〈111〉 is the polar direction. Ultrahigh strain levels up to 1.7%, an order of magnitude larger than those available from conventional piezoelectric and electrostrictive ceramics, could be achieved being related to an E-field induced phase transformation. High electromechanical coupling (k33)90% and low dielectric loss 1%, along with large strain make these crystals promising candidates for high performance solid state actuators.
Park et al. (1997) studied this question.