In order to explore the outstanding problems, such as poor mechanical performance, of recycled aggregate from construction waste in the application of backfills, this study innovatively used accelerated carbonation treatment technology to pretreat the recycled aggregates, and systematically investigated the evolution of mechanical properties in carbonated recycled aggregate-based cemented paste backfill (CPB). By carbonizing the waste recycled concrete aggregate (RCA), carbonation recycled concrete aggregates (CRCA) were obtained, and coal gangue was replaced as the filling aggregate at 50% and 100% for mine paste filling. The mechanical properties of the CPB were measured, and the mechanism was analyzed in combination with the changes in the microstructure. The results showed that the physical properties of RCA were significantly improved by carbonation treatment compared with untreated raw RCA: the apparent density of C60d-RCA increased by 2.88% relative to non-carbonated RCA, while its crushing value decreased by 51.45%, resulting in a more stable aggregate structure. In terms of mechanical properties, the compressive strengths of the 28day carbonated backfills with 50% and 100% CRCA contents (denoted as C28d-RCA-50 and C28d-RCA-100) reached 6.38 MPa and 5.32 MPa, representing increases of 61.52% and 46.33%, respectively, compared to the control group. Microstructure and phase composition analysis showed that the carbonation reaction not only produced calcium carbonate (CaCO3) crystals to effectively fill the internal pores and reduce the total porosity of the matrix, but also promoted the generation of monocarboaluminate and provided abundant nucleation sites for calcium silicate hydrate (C-S-H) gel hydration, which significantly optimized the structure of the interfacial transition zone (ITZ) and improved its microhardness. Among all test groups, the CRCA-50 group showed the most optimized microstructure and the best mechanical properties. This study provides a theoretical reference for the resource utilization of this type of 30-year service life RCA in mine filling.
Liu et al. (Sun,) studied this question.