In this study, a cellulose nanocrystal (CNC)-supported Ag–ZnO nanocomposite was synthesized via a hydrothermal route as a polymeric photocatalyst for efficient UV-A light-driven dye degradation. The renewable CNC framework provides abundant hydroxyl functional groups for nanoparticle anchoring, enhancing dispersion and interfacial charge transfer. Structural (XRD, FTIR, TEM, PL, and XPS) and thermal (TGA and DTG) analyses confirm successful incorporation of Ag nanoparticles and retention of CNC crystallinity. The composite exhibits a reduced optical bandgap (3.02 eV) and demonstrates superior photocatalytic activity, achieving 96% methylene blue (MB) degradation within 120 min. Enhanced performance is attributed to the synergistic effect of Ag-induced plasmonic excitation and CNC-facilitated charge migration, effectively suppressing ZnO photocorrosion. Moreover, the optimization of the parameters was conducted and found to be pH 7, a catalyst dose of 0.3 g L−1, and an initial MB concentration of 10 ppm, which shows the best photocatalytic degradation reaction. The CNC/Ag–ZnO catalyst maintains 87% activity after five reuse cycles, showing good stability and reusability. The photostability of the CNC/Ag–ZnO catalyst was evaluated by ICP-MS, which measured Zn2+ concentration in the aqueous solution. Additionally, the degraded MB compounds were identified using GC-MS/MS analysis. This work highlights the potential of polymer-based biogenic supports for sustainable photocatalyst design and bridges polymer science with environmental remediation technology.
Hossain et al. (Mon,) studied this question.