The influence of Cu content on the thermal conductivity and mechanical properties of Al-9Si-0.7Fe casting alloy were investigated in this paper. The results show that as the Cu content increases from 0.1 wt.% to 2.0 wt.%, the thermal conductivity of the alloy decreases from 173.6 W/(m·K) to 154.8 W/(m·K), while the yield strength increases from 72.2 MPa to 90.9 MPa. Metallographic, XRD, and EPMA analyses revealed that Cu has a relatively small impact on the secondary dendrite arm spacing of α-Al and the morphology of eutectic silicon. Its influence on the thermal conductivity and mechanical properties primarily stems from Cu atoms dissolving in the α-Al matrix, leading to a decreased lattice constant, increased lattice distortion, enhanced electron scattering, and improved solid solution strengthening effect. Based on the measured solubility of Cu, the Maxwell and Hashin–Shtrikman thermal conductivity models were modified. The correlation coefficients between the predicted values of the modified models and the experimental data were 92.77% and 93.11%, respectively, indicating a significant improvement in prediction accuracy.
Zhou et al. (Sun,) studied this question.