Dual characteristics of Mn 2+ dissolution from manganese oxide cathode materials in aqueous zinc batteries: trade-offs between active material loss and double capacity contribution
Perspective evaluates Mn2+ dissolution in Zn-MnO2 batteries, highlighting trade-offs in performance.
Key Points
This study aims to understand the dual characteristics of Mn2+ dissolution in aqueous Zn-MnO2 batteries regarding active material loss and capacity contribution.
Systematic evaluation of Mn2+ dissolution behavior in aqueous Zn-MnO2 batteries.
Analysis of the trade-offs between active material loss and double capacity contribution.
Mn2+ dissolution contributes to double capacity in batteries.
Active material loss due to Mn2+ dissolution significantly affects battery performance.