Effect of Mechanical Processing on Phase State and Microhardness of PSZ-Based Ceramics

EFFECT OF MECHANICAL PROCESSING ON THE PHASE STATE AND MICROHARDNESS OF PSZ-BASED COMPOSITE CERAMICS WITH AN Al2O3 ADDITION

View Full Paper
Ask AI
Bookmark
Share

Authors

IIIlya Timokhin Ilya

Discussion

Loading...

Member takes

Overview

Randomized trial reveals correlation between grinding depth and microhardness in zirconium-alumina ceramics, indicating their mechanical properties.

Key Points

  • This study aims to investigate the relationship between phase composition and microhardness of PSZ-based ceramics under different grinding depths.
  • Composite ceramics with 5.4 wt.% Y2O3 and 30 wt.% Al2O3 were analyzed.
  • Surface grinding was performed with a diamond wheel on an OSh-400 machine.
  • Microhardness was measured using the Vickers method and phase analysis by X-ray diffraction.
  • Increased grinding depth from 0.005 mm to 0.02 mm raised monoclinic zirconia content from 31% to 41%.
  • Microhardness decreased significantly from 15800 MPa to 14400 MPa as monoclinic phase content increased.
  • No changes in phase composition were detected at the minimum grinding depth of 0.005 mm.

Cite This Study

Ilya Timokhin Ilya (2026) studied this question.

synapsesocial.com/papers/6a1689eb0c924ddd1bd58868https://doi.org/10.62980/2076-0655-2026-108-117
View Full Paper
Ask AI
Bookmark
Share