The increasing demand for porous stainless-steel materials produced by selective laser melting (L-PBF) for biomedical implants, filtration systems, heat exchangers, and energy devices has created an urgent need to improve their mechanical performance. Optimizing process parameters and microstructural properties is therefore critical for enhancing the overall functionality and reliability of L-PBF porous stainless-steel structures. This paper studies the effect of an aging heat treatment on the mechanical properties of L-PBF specimens, manufactured with stainless steel Uddeholm Corrax powders. The porosity was selected to be about 3%, based on manufacturer’s experience on the production injection mold inserts, with the ability to drain air. To reach this porosity, a set of manufacturing variables were selected, quantified in terms of VED (Volumetric Energy Density) of 59.01 J/mm3. The analysis of the mechanical behavior was focused on the compressive and flexural strength, dynamic Young’s modulus and the energy dissipation during earlier fatigue loading cycles. This study concluded that the heat treatment produces a negligible effect on dynamic Young’s modulus and increases the bending strength by about 25% and the compressive plateau strength by about 17%. Both specimens’ batches exhibit similar fatigue strain accumulation for cyclic compressive tests.
Jesus et al. (Wed,) studied this question.