Crack growth behaviour of low-alloy steels for pressure boundary components under transient light water reactor operating conditions - CASTOC, part II: VVER conditions

One of the ageing phenomena of pressure boundary components of light water reactors (LWRs) is environmentally-assisted cracking (EAC). The project CASTOC (5 th Framework Programme of the EU) was launched September 2000 with six European partners and terminated August 2003. It focused in particular on the EAC behaviour of low-alloy steels (LAS) and to some extent to weld metal, heat affected zone and the influence of an austenitic cladding. The main objective was directed to the clarification of crack growth behavior of LAS in high-temperature water due to EAC under constant load (steady-state power operation), to study the effect of transient conditions (during operation or start-up/shut-down of a plant) using their impact on time-based and cycle-based crack growth rates and to a more detailed understanding of the acting mechanisms. Autoclave tests were performed with Western and Russian type reactor pressure vessel steels under simulated boiling water reactor (BWR)/normal water chemistry (NWC) and pressurized water reactor (VVER) conditions. The investigations were performed with fracture mechanics specimens of different sizes and geometries. The applied loading comprised cyclic loads, static loads and load spectra where the static load was periodically interrupted by partial unloading. With regard to water chemistry, the oxygen content (VVER) and impurities of sulphate and chlorides (BWR) were varied beyond allowable limits for continuous operation.The current paper summarizes the most important crack growth results obtained under simulated VVER conditions. The influence of oxygen content and the effect of specimen size (C(T)25 versus C(T)50 specimens) on the crack growth rates are shown. The results are discussed in the context of the current crack growth rate curves in the corresponding nuclear codes.