Research on the Microstructure and Performance Regulation of SLM 304 Steel Under Intermittent Deformation

This paper investigates the evolution of the microstructure, mechanical performances, and corrosion resistance of selective laser melting (SLM) 304 steel under different intermittent stretching deformation step sizes, revealing the underlying evolution patterns. The results indicate that the intermittent deformation step size significantly affects the microstructure and performance of SLM 304 steel. Larger step sizes result in more complete molten pool contours, less deformation of grain and cellular structures, and a lower martensite volume fraction; smaller step sizes lead to distorted molten pools, fragmented grains, exacerbated cellular structure distortion, and increased martensite content. In terms of mechanical performances, tensile strength, nano-hardness, and elastic modulus decrease with increasing step size, while elongation increases accordingly. Corrosion resistance improves with larger step sizes, with specimens exhibiting more complete and thicker oxide films on the surface and superior pitting resistance; continuous stretching specimens exhibit the worst corrosion resistance, while the original specimens are the best. Intermittent deformation optimizes properties by regulating microstructure, providing a basis for the design of high-performance SLM 304 steel. This study provides theoretical support for the design and application of additive manufacturing stainless steel components, facilitating the engineering and industrial application of SLM technology in high-end equipment manufacturing.